Bearing Grade PEEK
JUTAIPEEK?WR02 is a wear-resistant modified polyether ether ketone profile. WR stands for Wear resistance. WR02 is a PEEK product modified with 20% Teflon. Among them, Teflon is specially customized, which can achieve low lubrication coefficient and high anti-wear rate in the uniform dispersion of polyether ether ketone resin. The product has high abrasion resistance and also has the characteristics of not rubbing off powder. Suitable for electronic appliances, mechanical parts and other fields.?
Product Features
JUTAIPEEK?WR02 type Wear-resistance Grade PEEK profiles:
●Outstanding sliding and wear performance.
●Excellent strength and stiffness.
●Excellent dimensional stability and low thermal expansion.
●High thermal endurance and the long service temperature is 250℃.
●Outstanding chemical-resistance.
Application Fields
JUTAIPEEK?WR02 type Wear-resistance Grade PEEK profiles can be applied:?
——Electronics field;
——Mechanical Engineering Industry；
——Sealing Element Industry；
——Automotive Industry.
Instructions for Use
Machined by Lathes or Milling Machine.?
Remove surface heat-treatment aged layers and the thickness of removal layer is 0.5-1mm.
Product Storage Instructions
Placed away from light, avoiding humid, and away from oily substance.?
Packed with polymeric film when not use.
Product Technical Data
|
Performance
|
Test Method
|
Unit
|
Standard
|
|
Color
|
Eye
|
/
|
Rice-Yellow
|
|
Density
|
ISO 1183-1
|
g/cm3
|
1.40
|
|
Tensile Strength
|
ISO 527-2
|
MPa
|
≥78
|
|
Tensile Modulus
|
ISO 527-2
|
GPa
|
≥3.5
|
|
Elongation At Break
|
ISO 527-2
|
%
|
≥10
|
|
Charpy Impact Strength
|
ISO 179
|
kJ/m2
|
≥6.0
|
|
Flexural Strength
|
ISO 178
|
MPa
|
≥125
|
|
Flexural Modulus
|
ISO 178
|
GPa
|
≥3.2
|
|
Rockwell Hardness
|
ISO 2039-2
|
HRM
|
≥102
|
|
Melt Temperature
|
ISO 11357-3
|
℃
|
≥337
|
|
Thermal Conductivity
|
ISO 8302
|
W/(m?K)
|
≤0.82
|
|
Coefficient of Linear Thermal Expansion 20-100℃
|
ISO 11359-2
|
10-6/K
|
45-50
|
|
Long Service Temperature
|
UL 746B
|
℃
|
240
|
|
Heat Deflection Temperature
|
ISO 75-2
|
℃
|
260
|
|
Water Absorption （24h）
|
ISO 62
|
%
|
≤0.11
|
|
Flame Retardancy
|
UL 94
|
/
|
V-0
|
|
Frictional Coefficient
|
ASTM D3702
|
/
|
0.12
|
|
Wear Rate
|
mg/h
|
0.218
|
Notes: Frictional coefficient and wear rate were tested according to ASTM D3702, that is using thrust washer testing machine. Rubbing pair is PEEK sample thrust washer and 45# steel washer, and the contact area is 1.29cm2, and the inner diameter of the PEEK sample is 25mm. The applied load is 0.35MPa and the rubbing velocity is 2m/s.